Showing 20/20  |  Kendall τ: 0.8211 (p=4.61e-09, n=20)  |  MAE: 0.0278 eV/at

  ID  Formula      MLIP eV/at    Ref eV/at    Δ eV/at    MLIP#    Ref#  Dup
----  ---------  ------------  -----------  ---------  -------  ------  -----
3625  Si8             -5.4095      -5.4261    -0.0166        1       1  No
3603  Si8             -5.4062      -5.4189    -0.0127        2       2  No
1759  Si4             -5.4033      -5.4116    -0.0083        3       3  No
2589  Si6             -5.3259      -5.3698    -0.0439        4       4  No
3224  Si8             -5.3121      -5.3416    -0.0295        5       5  No
3424  Si8             -5.3083      -5.3221    -0.0138        6       6  No
3442  Si8             -5.2198      -5.1955     0.0243        7      10  No
2603  Si6             -5.2147      -5.2617    -0.047         8       7  No
2763  Si7             -5.2028      -5.2484    -0.0456        9       8  No
3286  Si8             -5.1758      -5.2155    -0.0397       10       9  No
1760  Si4             -5.1598      -5.0973     0.0625       11      17  No
2305  Si6             -5.1587      -5.1293     0.0294       12      13  No
2643  Si6             -5.1369      -5.1444    -0.0075       13      11  No
1618  Si4             -5.1313      -5.1306     0.0007       14      12  No
1594  Si4             -5.1289      -5.1212     0.0077       15      14  No
3005  Si7             -5.124       -5.0615     0.0625       16      20  No
 381  Si              -5.1233      -5.1087     0.0147       17      16  No
3059  Si7             -5.1233      -5.1092     0.0141       18      15  No
2308  Si6             -5.1199      -5.0715     0.0484       19      19  No
3238  Si8             -5.1193      -5.0926     0.0267       20      18  No